Physical and mechanical properties of continuous carbon or glass fiber reinforced endodontic posts are relevant to increase the retention and resistance of the tooth‐restoration system. Hollow posts have been recently designed for delivering the luting cement through the post hole, thus enhancing the post‐dentin interface by reducing the risk of air bubbles formation. Methods: Three type of endodontic posts, a carbon fiber hollow post, a glass fiber hollow post and a compact glass fiber post were investigated. Mechanical properties of these posts were assessed through bending tests. Teeth were subjected to fatigue cycling and the strength of restored teeth was detected through static tests. Failure modes were investigated through optical and scanning electron microscopy. Results show that composite posts increase the mechanical stability by more than 100% compared to premolars restored with particulate composite. Carbon fiber posts retain the highest strength (1467 N ± 304 N) among the investigated post and core restoration, but an unfavorable type of fracture has been observed, preventing the tooth re‐treatment. Instead, more compliant posts (i.e., glass fiber reinforced composite, providing a strength of 1336 N ± 221 N), show a favorable mode of fracture that allows the re‐treatment of teeth in the case that failure occurs. Glass fiber hollow posts show a good trade‐off between strength and a favorable type of fracture.

Fracture Strength and Failure Modes of Endodontically Treated Premolars Restored with Compact and Hollow Composite Posts Subjected to Cyclic Fatigue / Gallicchio, V.; Lodato, V.; De Santis, R.; Rengo, S.. - In: MATERIALS. - ISSN 1996-1944. - 15:3(2022), p. 1141. [10.3390/ma15031141]

Fracture Strength and Failure Modes of Endodontically Treated Premolars Restored with Compact and Hollow Composite Posts Subjected to Cyclic Fatigue

Gallicchio V.;Lodato V.;Rengo S.
2022

Abstract

Physical and mechanical properties of continuous carbon or glass fiber reinforced endodontic posts are relevant to increase the retention and resistance of the tooth‐restoration system. Hollow posts have been recently designed for delivering the luting cement through the post hole, thus enhancing the post‐dentin interface by reducing the risk of air bubbles formation. Methods: Three type of endodontic posts, a carbon fiber hollow post, a glass fiber hollow post and a compact glass fiber post were investigated. Mechanical properties of these posts were assessed through bending tests. Teeth were subjected to fatigue cycling and the strength of restored teeth was detected through static tests. Failure modes were investigated through optical and scanning electron microscopy. Results show that composite posts increase the mechanical stability by more than 100% compared to premolars restored with particulate composite. Carbon fiber posts retain the highest strength (1467 N ± 304 N) among the investigated post and core restoration, but an unfavorable type of fracture has been observed, preventing the tooth re‐treatment. Instead, more compliant posts (i.e., glass fiber reinforced composite, providing a strength of 1336 N ± 221 N), show a favorable mode of fracture that allows the re‐treatment of teeth in the case that failure occurs. Glass fiber hollow posts show a good trade‐off between strength and a favorable type of fracture.
2022
Fracture Strength and Failure Modes of Endodontically Treated Premolars Restored with Compact and Hollow Composite Posts Subjected to Cyclic Fatigue / Gallicchio, V.; Lodato, V.; De Santis, R.; Rengo, S.. - In: MATERIALS. - ISSN 1996-1944. - 15:3(2022), p. 1141. [10.3390/ma15031141]
File in questo prodotto:
File Dimensione Formato  
materials-15-01141-v2.pdf

accesso aperto

Tipologia: Versione Editoriale (PDF)
Licenza: Creative commons
Dimensione 27.42 MB
Formato Adobe PDF
27.42 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11588/884008
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 6
  • ???jsp.display-item.citation.isi??? 6
social impact