When amorphous poly(ethylene terephthalate) (I) yarns were annealed for a const. time at different temps., the degree of crystallinity increased with increasing temp. Unoriented samples began to crystallize at >100°; oriented samples crystd. at <100°. The faster crystallizability of oriented amorphous I at <110° showed a greater mol. mobility than that for unoriented amorphous I.
ON THE THERMAL-BEHAVIOR OF THE ORIENTED AMORPHOUS PHASE OF POLY(ETHYLENE-TEREPHTHALATE) / Busico, Vincenzo; Corradini, P; Riva, F; Seves, A; Vicini, L.. - In: DIE MAKROMOLEKULARE CHEMIE. RAPID COMMUNICATIONS. - ISSN 0173-2803. - STAMPA. - (1980), pp. 423-426.
ON THE THERMAL-BEHAVIOR OF THE ORIENTED AMORPHOUS PHASE OF POLY(ETHYLENE-TEREPHTHALATE)
BUSICO, VINCENZO;
1980
Abstract
When amorphous poly(ethylene terephthalate) (I) yarns were annealed for a const. time at different temps., the degree of crystallinity increased with increasing temp. Unoriented samples began to crystallize at >100°; oriented samples crystd. at <100°. The faster crystallizability of oriented amorphous I at <110° showed a greater mol. mobility than that for unoriented amorphous I.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.