1-Butene polyinsertion promoted by 2 typical C2-sym. zirconocene catalysts (i.e. rac-ethylenebis(1-indenyl)ZrCl2 and rac-dimethylsilylbis(1-indenyl)ZrCl2) was investigated under both hydrooligomerization and polymn. conditions and compared with that of propene. In spite of a similar regiospecificity for the 2 monomers, the fraction of dormant sites is higher in 1-butene polymn., as a result of a (much) lower reactivity of a 2,1 last-inserted unit. Accordingly, in the investigated cases, 2,1 units of 1-butene were not incorporated in the growing chains but either isomerized to 4,1 units or remained at the chain end until they underwent chain transfer via β-hydrogen elimination. Exptl. evidence is also presented of an epimerization reaction of the growing poly(1-butene) chain with a 1,2 last-inserted unit, leading to a decrease of polymer stereoregularity with decreasing monomer concn.
Isotactic 1-butene polymerization promoted by C2-symmetric metallocene catalysts / Borriello, Anna; Busico, Vincenzo; Cipullo, Roberta; Fusco, Ofelia; Chadwick John, C.. - In: MACROMOLECULAR CHEMISTRY AND PHYSICS. - ISSN 1022-1352. - STAMPA. - (1997), pp. 1257-1270.
Isotactic 1-butene polymerization promoted by C2-symmetric metallocene catalysts
BUSICO, VINCENZO;CIPULLO, ROBERTA;
1997
Abstract
1-Butene polyinsertion promoted by 2 typical C2-sym. zirconocene catalysts (i.e. rac-ethylenebis(1-indenyl)ZrCl2 and rac-dimethylsilylbis(1-indenyl)ZrCl2) was investigated under both hydrooligomerization and polymn. conditions and compared with that of propene. In spite of a similar regiospecificity for the 2 monomers, the fraction of dormant sites is higher in 1-butene polymn., as a result of a (much) lower reactivity of a 2,1 last-inserted unit. Accordingly, in the investigated cases, 2,1 units of 1-butene were not incorporated in the growing chains but either isomerized to 4,1 units or remained at the chain end until they underwent chain transfer via β-hydrogen elimination. Exptl. evidence is also presented of an epimerization reaction of the growing poly(1-butene) chain with a 1,2 last-inserted unit, leading to a decrease of polymer stereoregularity with decreasing monomer concn.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.