The magnetic field dependence of the elasticity moduli was measured in Fe73.5Cu1W3Si15.5B7 strips annealed in vacuum for 1 h from 400 degrees C to 500 degrees C. Maximum changes of the elasticity moduli (Delta E effect) from 83 to 158 GPa were observed after annealing at 400 degrees C. (C) 1998 Elsevier Science B.V. All rights reserved.
Heat-treatment dependence of the elasticity moduli and structure of Fe73.5Cu1W3Si15.5B7 alloy / Z., Kaczkowski; Lanotte, Luciano; M., Muller; P., Ruuskanen. - In: JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS. - ISSN 0304-8853. - STAMPA. - 185:(1998), pp. 109-111. [10.1016/S0304-8853(97)00270-9]
Heat-treatment dependence of the elasticity moduli and structure of Fe73.5Cu1W3Si15.5B7 alloy
LANOTTE, LUCIANO;
1998
Abstract
The magnetic field dependence of the elasticity moduli was measured in Fe73.5Cu1W3Si15.5B7 strips annealed in vacuum for 1 h from 400 degrees C to 500 degrees C. Maximum changes of the elasticity moduli (Delta E effect) from 83 to 158 GPa were observed after annealing at 400 degrees C. (C) 1998 Elsevier Science B.V. All rights reserved.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.