Elasticity moduli at constant magnetic field and at constant induction as the functions of magnetic bias field of the strips of Fe80B12Si8 metallic glass annealed in vacuum at temperatures of 370 and 380-degrees-C were investigated. The values of moduli in as-quenched state were changing from 133 to 155 GPa. After annealing at 370-degrees-C the moduli changes were from 80 to 170 GPa and after heat treatment at 380-degrees-C DELTAE effect increased and these changes were from 60 to 170 GPa.
Moduli of Elasticity of Fe80b12si8 Metallic-glass Strips Annealed To Vacuum At 370-degrees-c and 380-degrees-c / Z., Kaczkowski; Lanotte, Luciano. - In: IEEE TRANSACTIONS ON MAGNETICS. - ISSN 0018-9464. - STAMPA. - 30:(1994), pp. 1024-1026. [10.1109/20.312478]
Moduli of Elasticity of Fe80b12si8 Metallic-glass Strips Annealed To Vacuum At 370-degrees-c and 380-degrees-c
LANOTTE, LUCIANO
1994
Abstract
Elasticity moduli at constant magnetic field and at constant induction as the functions of magnetic bias field of the strips of Fe80B12Si8 metallic glass annealed in vacuum at temperatures of 370 and 380-degrees-C were investigated. The values of moduli in as-quenched state were changing from 133 to 155 GPa. After annealing at 370-degrees-C the moduli changes were from 80 to 170 GPa and after heat treatment at 380-degrees-C DELTAE effect increased and these changes were from 60 to 170 GPa.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.