This article reports a new way to prepare expanded graphite using a thermal method. Natural graphite was added to crystalline hydrate of metals with mechanical stirring at room temperature, taken in the number of 20-80% of the mass of mix. This was then placed in muffle furnace. All process of activation takes from 10 to 20 minutes. X-ray diffraction patterns were used to analyze the structure and confirm that expanded graphite had indeed been prepared. A scanning electron microscope was utilized to observe the morphologies of the expandable graphite and expanded graphite.
Preparation of Expanded Graphite Using a Thermal Method / Gulnura, Nyssanbayeva; Kenes, Kudaibergenov; Yerdos, Ongarbayev; Zulkhair, Mansurov; Di Capua, Roberto. - In: IOP CONFERENCE SERIES: MATERIALS SCIENCE AND ENGINEERING. - ISSN 1757-8981. - 323:1(2018), pp. 012012-1-012012-5. (Intervento presentato al convegno 1st International Conference on Functional Materials and Chemical Engineering, ICFMCE 2017 tenutosi a Dubai nel 2017) [10.1088/1757-899X/323/1/012012].
Preparation of Expanded Graphite Using a Thermal Method
Di Capua, Roberto
2018
Abstract
This article reports a new way to prepare expanded graphite using a thermal method. Natural graphite was added to crystalline hydrate of metals with mechanical stirring at room temperature, taken in the number of 20-80% of the mass of mix. This was then placed in muffle furnace. All process of activation takes from 10 to 20 minutes. X-ray diffraction patterns were used to analyze the structure and confirm that expanded graphite had indeed been prepared. A scanning electron microscope was utilized to observe the morphologies of the expandable graphite and expanded graphite.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.