In the present work, the synthesis of mesoporous material sieves in pure silica form (MCM-41 and MCM-48) and Al, Fe, Cu and Zn containing, having different pore diameters (corresponding to those between the upper limit for zeolites and the lower end of the mesoporous materials), high pore volumes (>0.8 cm3/g) and high specific surface areas (>1000 m2/g) is presented. The advantages of these materials in the adsorption technologies depend on their high specific surface area and pore volume as well as on the possibility to vary their pore size distributions under mild synthesis conditions and without post-synthesis treatments. The different capacities of CO2 sequestration of these mesoporous materials, with respect to the N2 adsorption capacities, at room temperature and pressure of 1 bar, were studied. The results show that these materials have high CO2 adsorption capacity and selectivity (ffi42 cm3/g and CO2/N2 ffi 22, respectively), and high working capacity (ffi17 cm3/g). These adsorption parameter values are comparable to those of the best adsorbents used in VSA processes.

Synthesis of mesoporous materials for carbon dioxide sequestration / Macario, A.; Katovic, A.; Giordano, G.; Iucolano, Fabio; Caputo, Domenico. - In: MICROPOROUS AND MESOPOROUS MATERIALS. - ISSN 1387-1811. - STAMPA. - 81:1-3(2005), pp. 139-147. [10.1016/j.micromeso.2005.02.002]

Synthesis of mesoporous materials for carbon dioxide sequestration

IUCOLANO, FABIO;CAPUTO, DOMENICO
2005

Abstract

In the present work, the synthesis of mesoporous material sieves in pure silica form (MCM-41 and MCM-48) and Al, Fe, Cu and Zn containing, having different pore diameters (corresponding to those between the upper limit for zeolites and the lower end of the mesoporous materials), high pore volumes (>0.8 cm3/g) and high specific surface areas (>1000 m2/g) is presented. The advantages of these materials in the adsorption technologies depend on their high specific surface area and pore volume as well as on the possibility to vary their pore size distributions under mild synthesis conditions and without post-synthesis treatments. The different capacities of CO2 sequestration of these mesoporous materials, with respect to the N2 adsorption capacities, at room temperature and pressure of 1 bar, were studied. The results show that these materials have high CO2 adsorption capacity and selectivity (ffi42 cm3/g and CO2/N2 ffi 22, respectively), and high working capacity (ffi17 cm3/g). These adsorption parameter values are comparable to those of the best adsorbents used in VSA processes.
2005
Synthesis of mesoporous materials for carbon dioxide sequestration / Macario, A.; Katovic, A.; Giordano, G.; Iucolano, Fabio; Caputo, Domenico. - In: MICROPOROUS AND MESOPOROUS MATERIALS. - ISSN 1387-1811. - STAMPA. - 81:1-3(2005), pp. 139-147. [10.1016/j.micromeso.2005.02.002]
File in questo prodotto:
File Dimensione Formato  
MMM 2005.pdf

non disponibili

Tipologia: Documento in Post-print
Licenza: Accesso privato/ristretto
Dimensione 393.15 kB
Formato Adobe PDF
393.15 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11588/204719
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 58
  • ???jsp.display-item.citation.isi??? 56
social impact