Catalysts for oxidative methanol reforming were prepared by thermal and H2-reduction treatments of a precursor consisting mainly of a hydrotalcite-like Cu–Zn–Al hydroxycarbonate and a Zn-rich paratacamite. The precursor was obtained by homogeneous precipitation of metal cations with a properly modified urea method. XRPD and quantitative Rietveld analysis of the precursor material revealed the presence of hydrotalcite and paratacamite phases in a weight ratio 3:1. Treatment in situ of the precursor produced Cu/ZnO/Al2O3 (Cu = 18%, Zn = 33%, Al = 49% mol) catalysts. Chemical properties of the precursor and of the catalysts were studied by TPR, TPO, NH3-TPD, N2O chemisorption, FTIR, and UV–vis techniques. Physical characterization was carried out by the SEM, EDS, XRPD, TG/DTA, and N2 adsorption techniques. The influence of heating rate of the precursor was investigated. Heat-treated samples contained CuO, ZnO, and amorphous Al2O3, and probably ZnAl2O4, as suggested by XRPD and FTIR measurements. The crystallinity of oxide phases was higher for the sample treated with a lower heating rate that also showed lower surface area and lower Cu dispersion. The presence of Cu2+ in octahedral sites of alumina was suggested by UV–vis spectra. CO adsorption gave evidence of easy reduction of Cu(II) to Cu(I) and Cu(0) and the formation of stable complexes with Cu(I). NH3-TPD and FTIR measurements showed the presence of surface acid sites of the Lewis type with wide strength distributions, mainly due to Zn2+ and Al3+ cations. Cu(II) was able to oxidize NH3, while Cu(0) activated NH3 decomposition. TPR and TPO measurements indicated that Cu species are easily reduced and reoxidized and Cu(I) species are intermediate for both processes. The redox properties appeared to be influenced by the rate of the previous heat treatment.

Production of hydrogen from oxidative steam reforming of methanol I. Preparation and characterization of Cu/ZnO/Al2O3 catalysts from a hydrotalcite-like LDH precursor / Turco, Maria; Bagnasco, Giovanni; U., Costantino; F., Marmottini; T., Montanari; G., Ramis; G., Busca. - In: JOURNAL OF CATALYSIS. - ISSN 0021-9517. - STAMPA. - 228:(2004), pp. 43-55.

Production of hydrogen from oxidative steam reforming of methanol I. Preparation and characterization of Cu/ZnO/Al2O3 catalysts from a hydrotalcite-like LDH precursor

TURCO, MARIA;BAGNASCO, GIOVANNI;
2004

Abstract

Catalysts for oxidative methanol reforming were prepared by thermal and H2-reduction treatments of a precursor consisting mainly of a hydrotalcite-like Cu–Zn–Al hydroxycarbonate and a Zn-rich paratacamite. The precursor was obtained by homogeneous precipitation of metal cations with a properly modified urea method. XRPD and quantitative Rietveld analysis of the precursor material revealed the presence of hydrotalcite and paratacamite phases in a weight ratio 3:1. Treatment in situ of the precursor produced Cu/ZnO/Al2O3 (Cu = 18%, Zn = 33%, Al = 49% mol) catalysts. Chemical properties of the precursor and of the catalysts were studied by TPR, TPO, NH3-TPD, N2O chemisorption, FTIR, and UV–vis techniques. Physical characterization was carried out by the SEM, EDS, XRPD, TG/DTA, and N2 adsorption techniques. The influence of heating rate of the precursor was investigated. Heat-treated samples contained CuO, ZnO, and amorphous Al2O3, and probably ZnAl2O4, as suggested by XRPD and FTIR measurements. The crystallinity of oxide phases was higher for the sample treated with a lower heating rate that also showed lower surface area and lower Cu dispersion. The presence of Cu2+ in octahedral sites of alumina was suggested by UV–vis spectra. CO adsorption gave evidence of easy reduction of Cu(II) to Cu(I) and Cu(0) and the formation of stable complexes with Cu(I). NH3-TPD and FTIR measurements showed the presence of surface acid sites of the Lewis type with wide strength distributions, mainly due to Zn2+ and Al3+ cations. Cu(II) was able to oxidize NH3, while Cu(0) activated NH3 decomposition. TPR and TPO measurements indicated that Cu species are easily reduced and reoxidized and Cu(I) species are intermediate for both processes. The redox properties appeared to be influenced by the rate of the previous heat treatment.
2004
Production of hydrogen from oxidative steam reforming of methanol I. Preparation and characterization of Cu/ZnO/Al2O3 catalysts from a hydrotalcite-like LDH precursor / Turco, Maria; Bagnasco, Giovanni; U., Costantino; F., Marmottini; T., Montanari; G., Ramis; G., Busca. - In: JOURNAL OF CATALYSIS. - ISSN 0021-9517. - STAMPA. - 228:(2004), pp. 43-55.
File in questo prodotto:
File Dimensione Formato  
JCatal1.pdf

non disponibili

Tipologia: Documento in Post-print
Licenza: Accesso privato/ristretto
Dimensione 519.02 kB
Formato Adobe PDF
519.02 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11588/202606
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact